Two visiting researchers are investigating the results of different treatment methods to improve the surface of molar-incisor-hypomineralisation (MIH)-affected teeth (Figure 2). Hardness is an important mechanical property of dental materials and is defined as the resistance to permanent surface indentation. Sufficient hardness ensures that the placed restorations are resistant to in-service scratching, from both mastication and abrasion. 

The instrument is configured to carry out two types of microhardness testing; Vickers and Knoop. In both methods a standardized load is applied to a fixed point on the sample. This creates a symmetrically shaped indentation, which can be measured and the hardness of the material calculated. In the Vickers hardness test, a diamond in the shape of a pyramid is used to make the indentation with a force load ranging from 100g to 30kg. In contrast, the diamond indenting tool used in the Knoop method is more narrow and elongated and a lower load is applied (20g to 2kg) (Figure 3).

Traditionally, Vickers is used to measure the hardness of very hard and brittle materials, such as cast dental alloys, but is also applicable to softer materials. Knoop has been used for a wider range of materials, from amalgam and ceramics to resin-based composites, but is also useful for materials that vary in hardness over an area of interest, such as enamel and dentin